Aluminum
Balls |
 |
Aluminum Balls
Aluminum balls are available in type 2017, 6061, and 7075.
Other aluminum alloys available upon request. They are
used in aircraft and automotive applications where weight is
a
factor or as a sealing ball to plug holes.
Aluminum 2017
|
Aluminum
2017 Balls Material Analysis |
| Silicon |
0.20 to 0.8 |
| Iron |
to 0.7 |
| Copper |
3.5 to 4.5 |
| Manganese |
0.40 to 1.0 |
| Magnesium |
0.40 to 0.8 |
| Chromium |
to 0.10 |
| Zinc |
to 0.25 |
| Titanium |
to 0.15 |
| Others |
to 0.05 |
| Aluminum
2017 Mechanical Properties |
| Temper |
O |
| Yield |
KSI 10
MPa 69 |
| Ultimate |
KSI 26
MPa 179 |
| Elongation / 4D |
22% |
| Hardness / Brinell 500kg 10mm |
45 |
| Ultimate Shearing Strenth |
KSI 18
MPa 124 |
| Fatigue / Endurance Limit - R.R. Moore
Type |
KSI 13
MPa 90 |
Aluminum 6061
|
Aluminum
6061 Material Analysis |
| Silicon |
0.40 to 0.8% |
| Iron |
to 0.7% |
| Copper |
0.15 to 0.40% |
| Manganese |
to 0.15% |
| Magnesium |
0.8 to 0.15% |
| Chromium |
0.04 to 0.35% |
| Zinc |
to 0.25% |
| Titanium |
to 0.15% |
| Others |
to 0.15% |
| Aluminum
6061 Mechanical Properties |
| Temper |
O |
| Yield |
KSI 8
MPa 55 |
| Ultimate |
KSI 18
MPa 124 |
| Elongation / 4D |
30% |
| Hardness / Brinell 500kg 10mm |
30 |
| Ultimate Shearing Strenth |
KSI 12
MPa 83 |
| Fatigue / Endurance Limit - R.R. Moore
Type |
KSI 9
MPa 62 |
Aluminum 7075
| Aluminum
7075 Ball Material Analysis |
| Silicon |
to 0.40% |
| Iron |
to 0.50% |
| Copper |
1.2 to 2.0% |
| Manganese |
to 0.30% |
| Magnesium |
2.1 to 2.9% |
| Chromium |
0.18 to 0.28% |
| Zinc |
5.1 to 6.1% |
| Titanium |
to 0.20% |
| Others |
to 0.15% |
| Aluminum
7075 Balls Mechanical Properties |
| Temper |
O |
| Yield |
KSI 15
MPa 103 |
| Ultimate |
KSI 33
MPa 228 |
| Elongation / 4D |
17% |
| Hardness / Brinell 500kg 10mm |
60 |
| Ultimate Shearing Strenth |
KSI 22
MPa 152 |
| Fatigue / Endurance Limit - R.R. Moore
Type |
----- |
Need more info on Aluminum balls?
|